Layered silicate nanocomposites based on various high-functionality epoxy resins: the influence of cure temperature on morphology, mechanical properties, and free volume
journal contribution
posted on 2003-03-11, 00:00 authored by O Becker, Y-B Cheng, Russell VarleyRussell Varley, G P SimonThis paper investigates the relationship between cure temperature, morphology, and mechanical properties of di-, tri-, and tetrafunctional high-performance, epoxy layered-silicate nanocompoaites. Wide-angle X-ray analysis (XRD) was carried out at different stages of cure to monitor organoclay exfoliation kinetics. It was found that some (small) degree of conversion was required to obtain significant intercalation. The nanocomposite morphology was also probed using transmission electron microscopy, XRD, and positron annihilation lifetime spectroscopy. The bifunctional DGEBA resin gave better exfoliation than the resins of higher functionalities. This is attributed to better catalysis of the intragallery reaction by the organo-ions which reside within the galleries. Higher cure temperatures were also found to improve clay delamination and simultaneously increased toughness and modulus in case of the DGEBA- and TGAP-based materials. Free volume properties did not vary significantly between resins or with cure temperature and generally followed the rule of mixtures, although there was a suggestion that the presence of clay leads to increased free volume. This was consistent with decreased glass transition temperatures upon addition of layered silicate, ascribed to disruption, and decreased cross-link density in interfacial regions of clay and epoxy matrix.
History
Journal
MacromoleculesVolume
36Issue
5Pagination
1616 - 1625Publisher
American Chemical SocietyLocation
Washington, D.C.Publisher DOI
ISSN
0024-9297eISSN
1520-5835Language
engPublication classification
C1.1 Refereed article in a scholarly journalCopyright notice
2003, American Chemical SocietyUsage metrics
Categories
No categories selectedKeywords
Licence
Exports
RefWorks
BibTeX
Ref. manager
Endnote
DataCite
NLM
DC