Solid state ion transport and phase behaviour in composites of N,N-methyl propylpyrrolidinium tetrafluoroborate and amorphous polyethylene oxide

The binary and ternary addition of 2 wt.% LiBF₄ and 2 wt.% amorphous polyethylene oxide (aPEO) respectively to the plastic crystal forming salt P₁₃BF₄ (where P₁₃⁺=methylpropyl pyrrolidinium cation) was investigated with specific focus on the phase behaviour and evaluation of transport characteristics. Differential scanning calorimetry (DSC), optical thermomicroscopy, solid state nuclear magnetic resonance (NMR), and AC impedance spectroscopy were used to develop an understanding of the conduction process in the pure and mixed systems. The morphology of the ternary compound appeared as hexagonal spherulites upon solidification. Multinuclear NMR Pulsed Field Gradient measurements (¹H,¹⁹F,⁷Li) to probe both cation and anion diffusion coefficients are reported. The anion is shown to be the most diffusive (at 320 K:¹⁹F=2.5×10⁻¹¹ m² s⁻¹; 1H: 1.8×10⁻¹¹ m² s⁻¹; ⁷Li: 1.1×10⁻¹¹ m² s⁻¹) in the ternary compound, with enhanced conductivity (2.7×10⁻⁵ S cm⁻¹ at 310 K) just below the melt.